Project Description
The R series of materials is an expression of our concern for the environment and our desire to make 3D printing as nature-friendly as possible.
R-PETG Impact filament is made from 100% recycled material. The recycled base material for R-PETG Impact is specially modified PET-G for increased impact strength (not recycled PET-G Standard). It is characterised by high impact strength, flexibility and heat resistance.
Like PET-G Standard, it is easy to print, causes no problems even for beginners, and is suitable for printing on popular 3D printer models without a heated chamber.
It can be successfully used for rapid prototyping and the printing of usable models.
R-PET-G Impact 3D filament has been manufactured from recycled material. Please note that each production batch of this material may vary slightly in colour intensity or shade. As a result, the colours of the prints may not be pure black or pure white, but present subtle variations in tones from dark grey to anthracite.
Diameter
Diameter
1.75 mmNet weight
Net weight
1000g (vacuum packed with a moisture absorber)Color
Color
GREAT PRECISION
NO ODOR
APPLICATION
APPLICATION
Prototypes, large-size prints, housings / shades, decorative elements.
HOW TO PRINT
HOW TO PRINT
Recommended printing temperature 230-260°C
Recommended table temperature: 60-80°C
Recommended cooling: 0-60%
The following parameters are only recommended print settings for this material. In order to achieve optimum print quality, it is recommended to adapt the settings to the specifications of the specific printer and the printing conditions.
TECHNICAL PARAMETERS
| Diameter | 1.75 mm |
| Diameter tolerance | +/- 0.05 mm |
| Oval tolerance | +/- 0.02 mm |
| Net weight | 1000g (vacuum packed with a moisture absorber) |
| Print temperature | 230-260 °C |
| Bed temperature | 60-80 °C |
For more details, such as the standards against which the tests were done, see the technical data sheet of the filament (TDS).
PHYSICAL PARAMETERS
| Density | 1,27-1,29 g/cm3 |
| Odor | Odourless |
| Tensile elongation | 4% |
| Tensile strength (to break) | > 42 MPa |
| Tensile modulus | 2020 MPa |
| Thermal deformation temperature | 63°C [ISO 75; 1,8 MPa] |
| Notched Izod impact strength | 5,5 kJ/m2 |
| Vicat softening point | 79°C |
| Charpy impact strength | 6,8 kJ/m2 |